STILL AT IT

There is a crazy rogue element in regards to testing, the bigger the test piece gets, the more unstable it (sometimes) becomes. What I mean to say is that the initial test of 50g comes out and lets me know if it is worth persuing. The next test is 250g and is on a guinomi or yunomi style pot. 99% of the time, everything is still on track at this point. Next comes the teabowl test and here is where thing just seem to go south. I am still unsure why the intitial tests work out fine only to be undone at the larger phase. Some do make it through the teabowl phase as well, only to be undone when the pot gets even bigger. I guess as I am working alot with ash glazes or glazes with ash in them, that the more vertical, the more the glaze runs and is altered tremendously as it pulls thin.

Fast forward to last week, I am still working on this psuedo-Jun-Yao glaze and trying to get it to stay on the pot and still have the characteristics that I am after.Tweak, tinker, alter and fingers crossed, I try again after a series of small tests and three days later, out come the results.Too little of this and the glaze is too dry, too much of that and the glaze runs unchecked right off the piece. Striking the right balance of adjustments, while maintaining the qualities that I am after is all about continued testing and just not knowing when to throw in the towel.

Illustrated is a large mentori guinomi fresh out of the kiln. It maintains that lavender, foamy quality with fine streaking where thick and it has wonderful breaking qualities. Where the glaze has run thin around the lip and at the edges of the facets, the glaze is an ashy clear that compliments the rest of the surface. Next step, again, on to a teabowl or two and we can see if I have solved the myriad of problems the glaze has already presented. I will let you know.

A BIZEN KILN

For your viewing pleasure, another  short video of the unloading of a nobori-gama. With the assistence of his family, students and employees of the kiln, Yoshimoto Syuho takes stock of his recent firing after cooling down for several days. Each firing is a major investment in time, energy and the production and expense of quite a few pots. This firing seems to have been quite sucessful.

Yoshimoto Syuho (b. 1938) is truly a veteran Bizen potter and studied under legendary master, Kaneshige Toyo. Though the Kaneshige legacy is apparent in the work and firing, Yoshimoto has carved out his own unique style and perspective of Bizen-yaki.

INKBLOT

Illustrated is a saffron (yellow iron) glazed teabowl with poured black and grey areas of slip over a white slipped body. The pouring is in fact, managed by using a squeeze bulb filled with the slip, to control the flow and to try to create a spontaneous, but not totally slipped area. The slips show well under my saffron  glaze and accentuate the vertical nature of the form while the irregular decoration helps animate the bowl and like any rorschach test, the viewer can see what ever reality they want in the surface.

"Reality has no inside, outside, or middle part."

                                                                            Bodhidharma

MELLOW YELLOW

There is just something evocative and timeless about Ki-Seto pottery. I am a big fan, though like most pottery styles, there are very few who have mastered the style and tradition. The finest Ki-Seto was arguably made by Arakawa Toyozo and in his hands, many of these pots have that quintessential Momoyama aire about them. The illustrated chawan is by Hori Ichiro, who creates exceptionally fine Ki-Seto pots, following in Arakawa's footsteps, as taught by his master, Kato Kozo.The form is directly related to Arakawa and Hori's use of exceptional materials and wood firing his pottery, just adds to the mystique and presence of his pots. One of the true attributes of Ki-Seto is that when used well, unlike other, heavy glazes, it still allows the clay to speak and the ability to see through the glaze and view each mark and line adds to the conversation from pot to viewer. The effort, energy and dedication of Hori to his work, is written in each and every pot.

"The mode by which the inevitable comes to pass is effort."

                                                                                      Oliver Wendell Holmes (1809-1994)

FROZEN FALLS

For a number of years while living in Plattsburgh, I was involved as a docent and research assistant at the Rockwell Kent Gallery at SUNY, Plattsburgh. I was enamored with Kent's painting/prints and style as well as the adventurous life he led. Among my favorite paintings are his winter landscapes and among those, FROZEN FALLS is my favorite. The balanced vertical element of the frozen falls against the horizontal motion of the clouds just appeals to me on a number of levels. For anyone who has been around dense vertical ice flows, like the one depicted in the painting, the color of the ice is striking and etches itself into your subconscious.

Since the image is copyrighted, if you wish to see the FROZEN FALLS painting, here is a link to it;    

http://clubs.plattsburgh.edu/museum/rkpnt22a.htm

Recently, I was able to handle a striking vase form by Iga master potter, Kishimoto Kennin. What immediately struck me was the resemblance it had to the FROZEN FALLS painting by Kent. The vase, made of wonderful Iga clay, is balanced with areas of hi-iro and the face of the piece displays a running stream of bidoro in its own way, a frozen fall created by the intense fire of an anagama rather than from canvas and oils and a vivid imagination.

OUT OF THE FIRE(PLACE)

"The main question today is: although we can make ash glazes without an excessive amount of effort, can we make ash glazed ware which is distinctive and also appropriate for both us and our times?"  Robert Tichane from his book; ASH GLAZES

My exposure to working with ash glazes and ash in glazes goes way back to the very beginning of my making pots. Collecting up various recipes along the way from Warren MacKenzie, Randy Johnston, Marie Woo, Kirk Mangus and many others, the real issue is what is the appropriate pot to use an ash glaze on. Not unlike copper red, determining where to use an ash glaze happens over time through trial and error of form, style and decoration. In time, a judicious use of an ash glaze is just as important as any other surface a potter can use. Ash glazes are not the answer to any and all pots.

Having moved away from strictly ash centered glazes, I have developed a palette of glazes that I have introduced ash to as a smaller percentage of the formula. With the use of ash in existing glazes, most recently, I have been able to come up with Ki-Seto, Karatsu and Tamba style effects. Given the sucess, now when testing glazes, I invariable make up the same formula with additions of 5% to 20% ash just to gauge the results and see what might occur. Some come out rather interesting, others not so much, but they is why it is called testing. The real plus to the ash addition is the runny factor, which I like very much. By putting an "ashed" glaze over a nice stiff glaze, I am able to get some significant amount of running, especially on more vertical forms. There is a very comforting connection from my beginning in pottery as well as the numerous stops along the way, that links up with how I work today when I use ash, right out of the fire(place).

The illustration is of  a stoneware mizusashi that was first glazed in a very thin ash glaze with .2% cobalt carbonate. Once mostly dry, I redipped it in a straight ash glaze to promote the running and mottling effects.

HIRADOBASHI

Illustrated is a very fine hanaire by legendary potter, Okabe Mineo (1919-1990). Made sometime during the mid-1960's, this hanaire is quintessential Okabe Ko-Seto style work and shows his profound knowledge of clay and ash glaze(s) that his is so well known for. In this particular form, the heavily textured clay is not masked with a dark and sometimes opaque Oribe, allowing for the Ko-Seto ash to animate the marks and run down the pot, accentuating the vertical nature of the piece. The varying tones of the glaze pool within texture creating a myriad of colors and fluidity that captures the movement of the vase. This hanaire is among one of the finest of this style that I have seen.

Like Tsukigata Nakiho's investigation, experimentation and mastery of Shino and Iron, Okabe Mineo focused on the use of ash and iron in glazes from 1947 on. It could possibly be a connection to the tradition of Seto where he was born, but his focus on ash was a major part of his use of clay and development of form. Okabe used ash in all of his glazes from Shino, Oribe, Ki-Seto, Ko-Seto and added iron as a major constituent of glazes to create his unique celadons including his trademark yohen beishokuji. His wonderful body of glazes based on ash and iron where further altered and rendered unique to Okabe by his skillful mastery of firing the kiln. His glazes would transmute in the kiln atmosphere in a style known as yohen (kiln change). The is no doubt that among Okabe Mineo's diverse legacy will be the broad and idiosyncratic body of glazes that he has left behind for collector and potter to study and contemplate in wonderment.

(The illustration is used with the kind permission of a collector, a friend, whose keen eye and passion for modern Japanese ceramics has put together an impressive collection. Several of the pots seen on my blog are from his collection.)

AN ORIBE ENIGMA

I have resolved myself to the fact that there will always be those Japanese pots that will remain unidentified. Sometimes it is as simple as not being able to read the cursive script on the box or being unable to identify a personal mark or seal. Other times, the pot arrives without a box and/or a mark obscurred by a layer of glaze. The illustrated large o-sara oribe tray form is just such an example of the later, no box, covered mark. I first came in contact with this piece about 5 or 6 years ago, I was struck by the strong form and wonderful visual texture skillfully glazed in an Oribe glaze. The way in which the glaze is applied makes full use of the crumbly texture and the quality clay, the tsuchi-aji ( flavor of the earth), shows through here and there as intended by the potter.  The clay appears to be a mix of Mino mogusa and Shigaraki clays, with most of the feldspar picked out of the mix before use.

This o-sara is very skillfully manipulated, textured, glazed and fired, though the maker remains a mystery, an enigma. It has qualities of Tsujimura Shiro, though I am unaware of an Oribe pieces of this style made by him. It also reminds me of the textured tray forms of Takeuchi Shugo that he creates by rolling out slabs and beating them with broken tree limbs, I even see elements of early Suzuki Goro. I am just not sure who made this piece, though that in no way detracts from the quality of the pot and the timeless pressence that it pocesses.

"By nature's kindly disposition most questions which it is beyond a man's power to answer do not occur to him at all."     George Santayana (1863-1952)

NARUMI-ORIBE

Illustrated is a close-up of a Narumi-Oribe basket form by Mino legend, Hayashi Shotaro (b. 1947).  This pot is an early work of Shotaro and clearly shows the indelible touch and influence of his elder brother and teacher Hayashi Kotaro (1940-1981). Shotaro spent a seven year apprenticeship with his brother before striking out and establishing his own studio/kiln in 1974. This piece demonstrates the traditional ideals passed down from teacher to student and a continuity of style and design shared by brothers.

Oribe ware in general has a whimsical quality to it and this basket is no exception. This practical, yet entertaining form, is a bit unique to Shotaro, though if you look hard enough, I think you will find the shape somewhere in antiquity. The spontaneous and asymmetrical designs  animates and accentuates this form, making for a pleasant visual and functional experience. Though made early in his career, it is obvious that Hayashi Shotaro has a keen grasp of form and surface as passed on from the tradition and his brother's thoughtful and insightful instruction.

"It takes an endless amount of history to make even a little tradition." Henry James (1843-1916)

SHIN-AO

I moved to the next step in testing with my new Oribe style glaze. I tempered the glaze a bit by adding .5% iron oxide and made up enough to glaze a few teabowls. Realizing that this new green can be rather bright over slip, I decided to use that to my advantage. I had thrown and severely paddled a group of bowls and took one and then poured white slip over either end of the ovalled form. Once bisque, I poured the glaze over the pot to vary thickness and then fired it in the last kiln firing. The illustrated teabowl is what I ended up with. The green is rich and bright over the white slip and a more somber green over the stoneware clay body. I find it rather nice that the glaze breaks to an almost clear over the raised ridges of the paddled texture, giving me three distinct colors on the teabowl. I think the developement of this new Oribe (Shin-Ao) is on track and may be destined for a larger bucket of glaze!

You can see more pictures of this chawan here;

http://www.trocadero.com/stores/albedo3studio/items/1129351/item1129351store.html

 "The combination of experience and experimentation will ultimately yield a personal sound."

                                                                                                                   Mark White (b. 1961)